Catalog No. | NC3489 |
---|---|
Size | Customized |
Material | Nickel Alloy |
Shape | Wire |
Haynes 214 Wire is a Nickel-Chromium-Aluminum-Iron alloy which is principally intended for use at temperatures of 955℃ (1750℉) and above. Stanford Advanced Materials (SAM) has rich experience in manufacturing and supplying high-quality Haynes 214 Wire.
Related products: HAYNES 188 Wire, Inconel 718 Wire, Inconel 600 Wire Mesh
Haynes 214 Wire is a Nickel-Chromium-Aluminum-Iron alloy that is principally intended for use at temperatures of 955℃ (1750℉) and above. It exhibits resistance to oxidation that far exceeds virtually all conventional heat-resistant wrought alloys at these temperatures.
Chemical Composition |
||
Element |
Min % |
Max % |
Al |
4.1 |
5 |
B |
– |
0.004 |
C |
– |
0.05 |
Nb/Cb |
– |
0.15 |
Co |
– |
2 |
Cr |
15 |
17 |
Fe |
2 |
4 |
Mg |
– |
0.01 |
Mn |
– |
0.5 |
Mo |
– |
0.5 |
Ni |
bal |
|
P |
– |
0.015 |
S |
– |
0.015 |
Si |
– |
0.2 |
Ti |
– |
0.5 |
W |
– |
0.5 |
Y |
0.003 |
0.04 |
Zr |
– |
0.02 |
Technical Data
Density |
8.05g/cm³ |
Melting Point |
1400°C |
Coefficient of Expansion |
13.3 μm/m °C (20 – 100°C) |
Modulus of Rigidity |
84 kN/mm² |
Modulus of Elasticity |
217 kN/mm² |
Our Haynes 214 Wire is carefully handled during storage and transportation to preserve the quality of our product in its original condition.
Please fill in your details and one of our material experts will get back to you within 24 hours. For more information, contact us via E-mail at sales@samaterials.com.
** Email address with your company's domain name is preferred. Otherwise, we may not be able to process your inquiry.